焊料熔化温度范围测试方法  

Testing Methods of Melting Temperature Range for Solders

作　　者：张红菊[1] 李璞[1] 沈磊[2] 郝雪龙[1] 燕鹏 

机构地区：[1]北京有色金属研究总院分析测试技术研究所,北京100088 [2]北京有色金属研究总院院务部,北京100088 [3]国核科学技术研究院,北京102209

出　　处：《理化检验（物理分册）》2015年第7期486-487,496,共3页Physical Testing and Chemical Analysis(Part A:Physical Testing)

摘　　要：熔化温度范围(包括固相线和液相线温度)是关系到焊料使用性能的基本参数之一,但目前对其测试的方法较多。对SJ/T 11390-2009,GB/T 1425-1996,JIS Z 3198-1-2003规定的不同方法进行了对比分析,并采用纯锡焊料进行了试验,发现按GB/T 1425-1996规定方法测试的液相线温度的相对误差较小,是更为准确的试验方法。Melting temperature range （including solidus and liquidus temperature） is one of the basic parameters of solder performance, however, there are many testing methods for determination of melting temperature, for example SJ/T 11390-2009, GB/T 1425--1996 and JIS Z 3198-1-2003. The differences among these methods were analyzed and discussed, the pure Sn solder was used for testing, and found that the testing relative error of liquidus temperature according to GB/T 1425- 1996 was smaller; the method specified in GB/T 1425- 1996 was more accurate.

关 键 词：焊料 熔化温度范围 固相线温度 液相线温度 标准 

分 类 号：TG42[金属学及工艺—焊接]