固体燃料和熔剂粒度对烧结生产影响的试验研究  

Experimental study on influences of solid fuel and flux size on sintering production

作　　者：刘自民[1] 金俊[1] 武轶[1] 李小静[1] 

机构地区：[1]马鞍山钢铁股份有限公司技术中心,安徽马鞍山243000

出　　处：《烧结球团》2015年第4期16-19,共4页Sintering and Pelletizing

摘　　要：在对马钢二铁总厂、三铁总厂烧结固体燃料、熔剂粒度组成多次实测的基础上,通过烧结杯试验,研究了固体燃料和熔剂粒度对烧结主要技术指标的影响。结果表明,当固体燃料和熔剂平均粒度分别为1.81 mm、1.68 mm时,烧结各项技术指标达到较佳平衡。本试验结果为马钢烧结调整优化固体燃料及熔剂粒度指明了方向,有助于马钢烧结矿产、质量的进一步提升。Based on actual measurement of sintering solid fuel and flux size distribution for No. 2 and No. 3 iron-making plant of Masteel many times,through sintering pot test, the influences of solid fuel and flux size on the main technical indexes of sintering were studied. The results show that,when the average particle size of solid fuel and flux is 1.81 mm and 1.68 mm respectively,the technical indexes of the sintering reach a good balance. The test results gives a clear direction for Masteel to adjust and optimize the solid fuel and flux size, and it helps to further promote Masteel sinter output and quality.

关 键 词：烧结试验 燃料粒度 熔剂粒度 

分 类 号：TF046.4[冶金工程—冶金物理化学]