水性聚氨酯缔合型增稠剂的制备及其工艺条件研究  

The Preparation and Process Conditions of Waterborne Polyurethane Associative Thickener

作　　者：郭玉珍[1] 王鸿儒[1] 张刚 赵鹏飞[1] 赵笑宇[1] 

机构地区：[1]陕西科技大学资源与环境学院,陕西西安710021 [2]佛山市三水协佳化工有限公司,广东佛山528000

出　　处：《塑料工业》2015年第10期23-26,47,共5页China Plastics Industry

摘　　要：以异氟尔酮二异氰酸酯(IPDI)为硬段,聚乙二醇(PEG)为软段,合成了一种聚氨酯缔合增稠剂(HEUR),并用FTIR对HEUR的结构进行了表征;研究了不同工艺条件对反应速率的影响,详细探讨了亲水链长度、原料配比及HEUR质量分数对增稠剂性能的影响。结果表明,当配比为IPDI∶PEG-6000∶正十六醇=2∶1∶2,催化剂的加入量0.2%时,预聚反应温度80℃,反应时间3 h;扩链反应温度为80℃,反应时间2 h;封端反应温度为80℃,反应时间3 h,为最优工艺条件。在此条件下,能够合成得到综合性能较好的缔合型聚氨酯增稠剂。Polyurethane associative thickener （HEUR） was synthesized with isophorone diisocynate （IPDI） as the hard segment and polyethylene glycol （PEG） as the soft segment, and HEUR＇s structure was characterized by Fourier transform infrared. The influences of different process conditions on the reaction rate were studied. The influences of hydrophilical chain length, the ratio of raw material and the mass ratio of HEUR on the thickening property were discussed in detail. Results showed that, with the ratio of IPDI ： PEG-6000 ： positive hexadecanol of 2 ： 1 ： 2, and the catalyst amount of 0. 2% , the pre-polymerization temperature was 80 ℃ and the reaction time was 3 h ; with extender chain reaction temperature of 80 ℃, the reaction time was 2 h; with sealing side reaction temperature of 80 ℃, the reaction time was 3 h, which were the optimal process conditions. Under the conditions, associative polyurethane thickener with comprehensive performance could be synthesized.

关 键 词：聚氨酯 缔合型 增稠剂 封端 增稠性能 

分 类 号：TQ637[化学工程—精细化工]