Synthesis and characterization of methacrylate matrix resin bearing o-nitrobenzyl group  

作　　者：郭玲香 管婧 林保平 杨洪 

机构地区：[1]School of Chemistry and Chemical Engineering, Southeast University

出　　处：《Journal of Central South University》2015年第9期3296-3301,共6页中南大学学报（英文版）

基　　金：Project(2008AA03323) supported by the High-Tech Research and Development of China;Project(21374016) supported by the National Natural Science Foundation of China;Project(BY201153) supported by Production,Forward-Looking Joint Research Project of Jiangsu Province,China

摘　　要：The matrix polymer PTBCHNB bearing o-nitrobenzyl group was successfully synthesized by copolymerization of tertiary-butyl methacrylate(TBMA), cyclohexyl methacrylate(CHMA) and o-nitrobenzyl methacrylate(NBMA) via reversible addition fragmentation chain transfer(RAFT) polymerization method. PTBCHNB was characterized by FTIR, 1HNMR, GPC and DSC. After UV irradiation, the o-nitrobenzyl groups of PTBCHNB were photocleaved and the resulting carboxyl groups were highly alkali soluble, and PTBCHNB was converted to PCHIBMA bearing carboxyl groups. So, the matrix polymer could be etched by mild alkali solution with no requirements of photoacid generators and other diverse additives. The photocleavable behaviors of PTBCHNB were determined by FTIR, 1H NMR and TGA analysis. The resist formulated with PTBCHNB and cast in THF solution showed square pattern of 10 μm×10 μm using a mercury-xenon lamp in a contact printing mode and tetramethyl-ammonium hydroxide aqueous solution as a developer.The matrix polymer PTBCHNB bearing o-nitrobenzyl group was successfully synthesized by copolymerization of tertiary-butyl methacrylate（TBMA）, cyclohexyl methacrylate（CHMA） and o-nitrobenzyl methacrylate（NBMA） via reversible addition fragmentation chain transfer（RAFT） polymerization method. PTBCHNB was characterized by FTIR, 1HNMR, ）GPC and DSC. After UV irradiation, the o-nitrobenzyl groups of PTBCHNB were photocleaved and the resulting carboxyl groups were highly alkali soluble, and PTBCHNB was converted to PCHIBMA bearing carboxyl groups. So, the matrix polymer could be etched by mild alkali solution with no requirements of photoacid generators and other diverse additives. The photocleavable behaviors of PTBCHNB were determined by FTIR, 1H NMR and TGA analysis. The resist formulated with PTBCHNB and cast in THF solution showed square pattern of 10 μm×10 μm using a mercury-xenon lamp in a contact printing mode and tetramethyl-ammonium hydroxide aqueous solution as a developer.

关 键 词：PHOTORESISTS o-nitrobenzyl methacrylate tertiary-butyl methacrylate reversible addition fragmentation chain transfer 

分 类 号：TQ316.3[化学工程—高聚物工业]