Mechanism of hot-rolling crack formation in lean duplex stainless steel 2101  

作　　者：Zhi-hui Feng Jing-yuan Li Yi-de Wang 

机构地区：[1]School of Materials Science and Engineering, University of Science and Technology Beijing

出　　处：《International Journal of Minerals,Metallurgy and Materials》2016年第4期425-433,共9页矿物冶金与材料学报（英文版）

基　　金：financially supported by the National Natural Science Foundation of China (No. 51174026);the National Science and Technology Pillar Program during the Twelfth Five-Year Plan Period (No. 2012BAE04B02)

摘　　要：The thermoplasticity of duplex stainless steel 2205（DSS2205） is better than that of lean duplex steel 2101（LDX2101）, which undergoes severe cracking during hot rolling. The microstructure, microhardness, phase ratio, and recrystallization dependence of the deformation compatibility of LDX2101 and DSS2205 were investigated using optical microscopy（OM）, electron backscatter diffraction（EBSD）, Thermo-Calc software, and transmission electron microscopy（TEM）. The results showed that the phase-ratio transformations of LDX2101 and DSS2205 were almost equal under the condition of increasing solution temperature. Thus, the phase transformation was not the main cause for the hot plasticity difference of these two steels. The grain size of LDX2101 was substantially greater than that of DSS2205, and the microhardness difference of LDX2101 was larger than that of DSS2205. This difference hinders the transfer of strain from ferrite to austenite. In the rolling process, the ferrite grains of LDX2101 underwent continuous softening and were substantially refined. However, although little recrystallization occurred at the boundaries of austenite, serious deformation accumulated in the interior of austenite, leading to a substantial increase in hardness. The main cause of crack formation is the microhardness difference between ferrite and austenite.The thermoplasticity of duplex stainless steel 2205（DSS2205） is better than that of lean duplex steel 2101（LDX2101）, which undergoes severe cracking during hot rolling. The microstructure, microhardness, phase ratio, and recrystallization dependence of the deformation compatibility of LDX2101 and DSS2205 were investigated using optical microscopy（OM）, electron backscatter diffraction（EBSD）, Thermo-Calc software, and transmission electron microscopy（TEM）. The results showed that the phase-ratio transformations of LDX2101 and DSS2205 were almost equal under the condition of increasing solution temperature. Thus, the phase transformation was not the main cause for the hot plasticity difference of these two steels. The grain size of LDX2101 was substantially greater than that of DSS2205, and the microhardness difference of LDX2101 was larger than that of DSS2205. This difference hinders the transfer of strain from ferrite to austenite. In the rolling process, the ferrite grains of LDX2101 underwent continuous softening and were substantially refined. However, although little recrystallization occurred at the boundaries of austenite, serious deformation accumulated in the interior of austenite, leading to a substantial increase in hardness. The main cause of crack formation is the microhardness difference between ferrite and austenite.

关 键 词：duplex stainless steel hot rolling crack formation THERMOPLASTICITY grain size PRECIPITATES softening mechanisms 

分 类 号：TG335.11[金属学及工艺—金属压力加工] TG142.71[一般工业技术—材料科学与工程]