复合材料受损板的结构分析与强度预测  

Structural Analysis and Strength Prediction of the Damaged Composite Plate

作　　者：李路可[1] 王雪峰[1] 沈华刚[1] 

机构地区：[1]郑州科技学院,河南郑州450064

出　　处：《机械研究与应用》2016年第4期149-150,154,共3页Mechanical Research & Application

基　　金：河南省科技厅自然科学项目(编号:152102210174)

摘　　要：基于三维逐渐损伤理论,通过采用ANSYS二次开发语言APDL,建立了含孔复合材料层合板的三维有限元模型,通过对层合板进行施压,综合考虑了层合板基体开裂、基纤剪切、分层和纤维断裂四种主要失效模式,并基于刚度退化准则,分析了复合材料层合板内部损伤的产生和扩展过程,求出了层合板的最终失效值。Based on the three-dimensional progressive damage theory, a three-dimensional finite elemental model of hole incomposite is built by using the secondary development language of the ANSYS software. Through the study of pressing the lam-inate plate, and considering the four main failure modes of the matrix cracking, shear-based fiber, delamination and fiberbreakage, the production and the expansion process of interior damage and the gradual destruction of the composite laminatedplates under compressive load are analyzed based on the stiffness degradation criterion. Finally, the final failure value of thecomposite laminated plates with holes is calculated.

关 键 词：复合材料层合板 三维累计损伤 刚度退化 失效分析 

分 类 号：TB302[一般工业技术—材料科学与工程]