模板法研制有序介孔SiO_2膜及其性能表征的研究  

Template Development Ordered Pore and Characterization of SiO_2 film

作　　者：许秀玲[1] 

机构地区：[1]潍坊科技学院,山东寿光262700

出　　处：《化工设计通讯》2016年第7期114-114,共1页Chemical Engineering Design Communications

摘　　要：采用模板法研制了有序介孔SiO2膜，探讨了其性能表征。在研究中采用了正硅酸乙酯（TEOS）与十六烷基三甲基氯化铵（CTAC），在致密基底上，研制了有序介孔SiO2膜，观察了CTAC/TEOS摩尔比对SiO2膜孔径及其介孔有序性的影响，实验结果证实，有序介孔SiO2膜的孔径在2～3nm，呈单一分布，孔体积随着CTAC/TEOS摩尔比增加而增大，CTAC/TEOS摩尔比为0.35时，SiO2膜的渗透率最大。In this paper,template method,developed mesoporous SiO2 film explores its characterization.In the study using TEOS（TEOS）and cetyl trimethyl ammonium chloride（CTAC）,on the dense substrate is developed mesoporous SiO2 membrane were observed CTAC/TEOS molar ratio of aperture orderliness impact mesoporous SiO2 film and experimental results confirmed that the mesoporous SiO2 membrane pore size in 2~3nm,showed a single distribution,pore volume with CTAC/TEOS molar ratio increases and increases,CTAC/TEOS molar ratio of 0.35,the amount of SiO2 membrane permeability maximum.

关 键 词：模板法 有序介孔 SIO2膜 性能表征 