电子级玻璃纤维布表面处理研究  

Study on Surface Treatment of Electronic-grade Glass Fabrics

作　　者：张志坚 王富峰 杜家奎 姚慧 李焕兴 宋长久 Zhang Zhijian Wang Fufeng Du Jiakui Yao Hui Li Huanxing Song Changjiu(Jushi Group Co., Ltd., Tongxiang 314500)

机构地区：[1]巨石集团有限公司,桐乡314500

出　　处：《玻璃纤维》2017年第2期6-8,13,共4页Fiber Glass

摘　　要：采用正交试验的方法研究了电子布表面处理过程中生产车速、开纤压力、布面烘干温度和处理剂配方对电子布性能的影响程度,确定影响试验结果的各个因子的主次顺序,通过调整主要的影响因子来提高电子布的含浸性和减少板材干花比例,并成功解决了高粘度酚醛环氧树脂胶系板材的干花问题。The influences of production speed, spunlacing pressure, fabric drying temperature and treament agents on the properties of electronic-grade glass fabrics were studied by orthogonal tests. The major and minor factors af- fecting the test results were determined. By adjusting the major impacting factors, the impregnation of these glass fabrics was improved ,the proportion of CCL with dry spots was reduced, and the defect of dry spots on CCL made from high-viscosity phenolic epoxy resin was successfully solved.

关 键 词：电子布 表面处理 覆铜板 正交试验法 

分 类 号：TQ171.774.2[化学工程—玻璃工业]