作 者:曲红梅[1] 杨巍[1] 马永刚[1] 马芮[2] QU Hong-mei YANG Wei MA Yong-gang MA Rui(Department of Stomatology, Tsinghua University YuQuan Hospital, Beijing 100039, China)
机构地区:[1]清华大学玉泉医院口腔科,副主任医师北京100039 [2]中国医学科学院北京协和医院口腔科,医师北京100730
出 处:《口腔颌面修复学杂志》2017年第4期224-227,共4页Chinese Journal of Prosthodontics
基 金:北京石景山区医学重点扶持专科建设工作方案(项目编号:20170010)
摘 要:目的:探讨氧化锆表面粗糙度对树脂水门汀剪切粘接强度的影响。方法:将55个氧化锆瓷块随机分为5组,分别用120#、240#、360#、500#、600#砂纸打磨瓷块表面,扫描电镜观察表面形态。将每组试样与Multilink N通用型树脂水门汀粘接后,万能试验机测试剪切粘接强度,并对结果进行单因素方差分析等统计学分析。结果:120#、240#、360#、500#、600#五组的剪切粘接强度分别为11.031±0.902MPa、11.592±1.045MPa、13.380±1.171MPa、11.640±0.957MPa和10.588±1.249MPa。单因素方差分析结果显示5组试样的总体均数不等,360#组的剪切强度值高于其他各组,P<0.05;120#、240#、500#、600#组间差异无统计学意义,P>0.05。结论:表面粗糙度是氧化锆陶瓷与树脂水门汀之间剪切粘接强度的相关影响因素,360#砂纸打磨形成的表面粗糙度可提供最大的树脂水门汀剪切粘接强度。Objective: To evaluate the effects of surface roughness of zirconia on the shear bond strength of resin cements. Methods: 55 zirconia specimens were randomly divided into 5 groups. Single surface of each sample was polished with 120#, 240#, 360#, 500#, 600# sand paper respectively. The surface of the specimen was observed by scanning electron microscopy (SEM). Ten specimens each group were bonded with Multilink N resin cement and subjected to shear bond strength test. The value of shear bond strength was measured, and statistically analyzed with SPSS 19.0. Results: The shear bond strength after treating with 120#, 240#, 360#, 500# and 600# were 11.031±0.902 MPa, 11.592± 1.045 MPa, 13.380±1.171 MPa, 11.640±0.957 MPa and 10.588±1.249 MPa respectively. The result of one-way ANOVA showed that the means of 5 groups of specimens were not equal, and the shear bond strength of 360# was significantly higher than that of the other 4 groups (P〈 0.05); there was no significant difference between the other 4 groups (P〉 0.05). Conclusion: The surface roughness is related to the shear bond strength between zirconia ceramic and resin cement. The surface roughness formed by 360# sand paper provides the maximum shear bond strength of resin cements in the study.
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在链接到云南高校图书馆文献保障联盟下载...
云南高校图书馆联盟文献共享服务平台 版权所有©
您的IP:216.73.216.229