纯天然胡麻胶的提取工艺优化及化学改性研究  

Study on extraction technology optimization and chemical modification of flaxseed gum

作　　者：张印红[1] 赵春生[1] 方涛 毛勇坡 李筱然 王彦斌[1] ZHANG Yin-hong, ZHAO Chun-sheng, FANG Tao, MAO Yong-po, LI Xiao-ran(College of Chemical Engineering, Northwest Minzu University, Lanzhou 730000, Chin)

机构地区：[1]西北民族大学化工学院,甘肃兰州730000

出　　处：《精细与专用化学品》2018年第3期36-38,共3页Fine and Specialty Chemicals

基　　金：西北民族大学国家级大学生创新创业训练计划资助项目(201710742079)

摘　　要：以甘肃本地胡麻籽为原料,采用蒸馏水直接浸提法提取胡麻胶,并对提取工艺进行优化。以提取时间、料液比、温度三个主要因素进行单因素试验研究,并将提取的胡麻胶配制成质量分数为1%的溶液进行化学改性实验。实验结果表明,胡麻胶最佳提取工艺条件为:料液比为1g胡麻籽用11mL蒸馏水、温度75℃、时间90min时,胡麻胶的提取率为7.75%。通过化学改性后测得接枝率为5.3%,在一定程度上提高了胡麻胶的耐水性。Flaxseed gum extracted from flaxseed in Gansu province by direct extraction of distilled water were studied.The optimum extraction conditions were as follows：solid-liquid ratio 1∶11（g/mL）,temperature 75℃,time 90 min,the extraction rate of flaxseed gum was 7.75%.After chemical modification,the grafting rate was 5.3%,which improved the water resistance of flaxseed glue.