NMP中制备TiO_2溶胶及其凝胶化  

Preparation of TiO_2 Sol in NMP and Its Gelation

作　　者：杜宏伟[1] 孔瑛[1] 

机构地区：[1]石油大学化学化工学院,东营257061

出　　处：《应用化学》2002年第9期882-885,共4页Chinese Journal of Applied Chemistry

基　　金：科技部国家重点基础研究发展规划项目 (G2 0 0 0 0 2 64 0 7);山东省自然科学基金 (0 97B0 2 12 2 );中国石油天然气集团公司石油科技中青年创新基金资助项目

摘　　要：用钛酸丁酯作前驱物 ,N-甲基吡咯烷酮 (NMP)作溶剂 ,冰乙酸为稳定剂 ,通过溶胶 -凝胶法制得了Ti O2 溶胶。通过加水方式 ,加水量 ,溶剂量 ,p H值和温度等因素对 Ti O2 溶胶 -凝胶过程影响的实验。得出了在 NMP中制备稳定 Ti O2 溶胶的最佳条件。结果表明 ,室温下 ,当 NMP与钛酸丁酯的体积比为 2～ 3 ;V(水 ) /V(钛酸丁酯 )为 3～ 4;p H值为 2～ 4时所得 Ti O2 溶胶稳定 ,透明性好。TiO 2 sol was prepared in NMP by a sol gel method using tetrabutyl titanate(TBT) as a precursor and acetic acid as a stabilizer. The effects of reaction conditions e.g. the way of adding water, mole ratio of water to TBT, volume ratio of NMP to TBT, pH value and temperature on the sol gel process have been investigated. The results showed that at room temperature when the mole ratio of water to TBT was 3~4, the volume ratio of NMP to TBT was 2~3 and the value of pH was 2~4 a stable and transparent TiO 2 sol could be obtained.

关 键 词：凝胶化 TIO2溶胶 NMP 溶胶-凝胶过程 二氧化钛 N-甲基吡咯烷酮 钛酸丁酯 

分 类 号：O614.411[理学—无机化学] O648.17[理学—化学]