Epitaxial growth and oxidation behavior of an overlay coating on a Ni-base single-crystal superalloy by laser cladding  

作　　者：Jingjing Liang Yongsheng Liu Jinguo Li Yizhou Zhou Xiaofeng Sun 

机构地区：[1]Institute of Metal Research, Chinese Academy of Sciences [2]State Key Laboratory of Solidification Processing, Northwestern Polytechnical University [3]Space Manufacturing Technology (CAS Key Lab)

出　　处：《Journal of Materials Science & Technology》2019年第2期344-350,共7页材料科学技术（英文版）

基　　金：financially supported by the National Natural Science Foundation of China (NSFC) under grant Nos. 51771190, 51401210, U1508213, 51701210, 51871221;the National High Technology Research and Development Program (863 Program, No. 2014AA041701);the fund of the State Key Laboratory of Solidification Processing in NWPU (SKLSP201834);the Theme Special Project of Shenyang Key Science and Technology Research and Development Programs (17-85-0-00)

摘　　要：An overlay coating material was deposited on a single crystal superalloy SRR99 by laser cladding.The microstructure and oxidation behavior of this coating was investigated through scanning electron microscopy(SEM) and X-ray diffraction(XRD). The results indicated that although the composition of the coating was chosen based on the γ' composition in René N5 superalloy, the primary solidification phase of this coating during laser cladding was γ-Ni. Furthermore, under the laser cladding condition, fine parallel dendrites grew epitaxially in the coating from the substrate, indicating the single crystal structure of the substrate was reproduced. When the single crystal MCrAlY coating was oxidized at 1000?, both Al_2O_3 and Al_2O_3 formed during initial oxidation process. As the oxidation time proceeded, the presence of Al_2O_3 facilitated the formation of NiAl_2O_4 spinel oxide. Once the spinel was observed, it flourished and induced some porosity in the scale. When the scale thickness increased to 6–7 μm, large area spallation of the scale began.An overlay coating material was deposited on a single crystal superalloy SRR99 by laser cladding.The microstructure and oxidation behavior of this coating was investigated through scanning electron microscopy(SEM) and X-ray diffraction(XRD). The results indicated that although the composition of the coating was chosen based on the γ' composition in René N5 superalloy, the primary solidification phase of this coating during laser cladding was γ-Ni. Furthermore, under the laser cladding condition, fine parallel dendrites grew epitaxially in the coating from the substrate, indicating the single crystal structure of the substrate was reproduced. When the single crystal MCrAlY coating was oxidized at 1000?, both Al_2O_3 and Al_2O_3 formed during initial oxidation process. As the oxidation time proceeded, the presence of Al_2O_3 facilitated the formation of NiAl_2O_4 spinel oxide. Once the spinel was observed, it flourished and induced some porosity in the scale. When the scale thickness increased to 6–7 μm, large area spallation of the scale began.

关 键 词：Laser CLADDING Single crystal growth EPITAXY OVERLAY COATING 

分 类 号：TG[金属学及工艺]