316奥氏体不锈钢中厚板轧制晶粒度控制研究  

Research on Grain Size Control of 316 Austenitic Stainless Steel Heavy and Medium Plate Rolling

作　　者：杨相歧 庄迎[2] 李吉东[2] 尹嵬 Yang Xiangqi;Zhuang Ying;Li Jidong;Yin Wei(Lisco Branch Company, Shanxi Taigang Stainless Steel Co. , Ltd. , Linfen 041000;Technology Center, Shanxi Tai gang Stainless Steel Co. , Ltd. , Taiyuan 030003)

机构地区：[1]山西太钢不锈钢股份有限公司临汾分公司,临汾041000 [2]山西太钢不锈钢股份有限公司技术中心,太原030003

出　　处：《特殊钢》2019年第3期70-73,共4页Special Steel

摘　　要：针对316不锈钢中厚板晶粒度控制问题在实验室进行了一系列的轧钢试验,分别对钢坯原始组织状态、总轧制压缩比、单道次变形率3个因素进行分析。试验结果表明,当轧制压缩比超过6时,钢坯原始组织状态对中厚板全厚度晶粒均匀性无明显影响;钢坯加热温度、道次压下量相同时,总压缩比为6生产工艺能够轧制出全厚度晶粒均匀的钢板;当轧制总压缩比为4时,单道次压下率超过30%时,钢板表面晶粒度为2级和7级混晶组织;单道次轧制变形量均小于10%时,即使轧制总压缩比足够大,钢板热轧态晶粒度依然不均匀。The influence of the status of billet steel, rolling compression ratio, deformation rate per pass on grain of 316 austenitic stainless steel medium plate was done in laboratory.The results explaine that the total compression ratio is more than 6, the original structure of steel billet has no influence on grain size of hot rolling plate, when the total compression ratio is more than 6, the homogeneous grain in the whole thickness is obtained in condition of same billet steel heatingup temperature and deformation rate per pass.But when the total compression ratio is more than 6, the 2 grade and 7 grade duplex grain are obtained even though the deformation rate per pass is more than 30%, and when the total compression ratio is less than 10%, the grain is heterogeneous even though the total compression ratio is big enough.

关 键 词：316不锈钢中厚板 热轧 晶粒度 变形率 

分 类 号：TG335.51[金属学及工艺—金属压力加工]