在环氧富锌底漆+丙烯酸聚氨酯面漆体系的应用中以粉末涂料替代溶剂型涂料  

Substitution of solvent-based paints by powder paints in the application of zinc-rich epoxy primer plus acrylic polyurethane topcoat system

作　　者：李宾[1] 田兴强[1] 史忠震[1] LI Bin;TIAN Xing-qiang;SHI Zhong-zhen(Guizhou Jiaotong College,Guiyang 550008,China)

机构地区：[1]贵州交通职业技术学院

出　　处：《电镀与涂饰》2019年第18期995-998,共4页Electroplating & Finishing

摘　　要：考察了静电喷涂粉末涂层的厚度与其耐蚀性的关系。结果表明,仅采用120~140μm的丙烯酸聚氨酯粉末面漆时,涂层的耐盐雾腐蚀能力与按一般防腐要求喷涂的溶剂型涂料体系的性能相当。当环氧富锌粉末底漆膜厚为40~60μm,总厚度控制在100~180μm时,底+面粉末涂层体系的耐盐雾腐蚀能力与按重防腐要求喷涂的溶剂型涂料体系的性能相当。The relationship between the thickness of electrostatic powder coating and its corrosion resistance was studied.The results showed that the acrylic polyurethane powder topcoat with a thickness of 120-140μm had an equivalent salt spray corrosion resistance to a solvent-based coating system for general anticorrosion applications.The primer and topcoat powder system with a primer thickness of 40-60μm and a total thickness of 100-180μm had an equivalent salt spray corrosion resistance to the solvent-based coating system for heavy-duty anticorrosion applications.

关 键 词：环氧底漆 丙烯酸聚氨酯面漆 粉末静电喷涂 溶剂型涂料 膜厚 耐蚀性 

分 类 号：TQ639[化学工程—精细化工]