聚苯硫醚砜纤维和聚芳砜纤维的制备及其性能研究  

Study on preparation and properties of polyphenylene sulfide sulfone and polyarylsulfone fibers

作　　者：高路遥 王明稳 苏坤梅[1] 李振环[2] GAO Luyao;WANG Mingwen;SU Kunmei;LI Zhenhuan(State Key Laboratory of Separation Membranes and Membrane Processes of National Center for International Joint Research on Separation Membranes,School of Environment Science and Engineering,Tianjin Polytechnic University,Tianjin 300387;State Key Laboratory of Separation Membranes and Membrane Processes of National Center for International Joint Research on Separation Membranes,School of Material Science and Chemistry Engineering,Tianjin Polytechnic University,Tianjin 300387)

机构地区：[1]天津工业大学环境科学与工程学院天津工业大学省部共建分离膜与膜过程国家重点实验室,天津300387 [2]天津工业大学材料科学与工程学院天津工业大学省部共建分离膜与膜过程国家重点实验室,天津3003871

出　　处：《合成纤维工业》2019年第5期7-11,共5页China Synthetic Fiber Industry

基　　金：国家自然科学基金面上(21878231);中石化科技开发项目(216090,218006-8);天津市自然科学基金重点项目(15JCZDJC37000);中国纺织工业联合会应用基础研究项目(J201406)

摘　　要：以2.0 dtex、51mm的聚苯硫醚(PPS)纤维为原料,以双氧水为氧化剂、冰乙酸为催化剂,对PPS纤维进行氧化改性处理,通过改变氧化反应温度和反应时间等工艺条件,制备聚苯硫醚砜(PPSO)纤维和聚芳砜(PASO)纤维,并对改性纤维的结构形貌及性能进行表征。结果表明:在双氧水:蒸馏水:冰乙酸质量比为50:25:25、氧化反应时间为5 h的条件下,当氧化反应温度为25~60℃时得到PPSO纤维,当氧化反应温度升高至80℃时得到PASO纤维;氧化改性过程中,伴随着硫(S)原子流失和聚芳烃的生成,改性纤维中出现大量氧(O)元素,证明PPS纤维被成功氧化改性;氧化处理对纤维的表面形貌影响不大,但纤维力学性能降低;经硝酸溶液浸泡处理后,PPS纤维强度保持率为79.8%,而PASO纤维强度保持率提高到112.2%, PPSO纤维强度保持率高达138.1%,说明氧化改性后的PPS纤维抗氧化能力明显提高。Polyphenylene sulfide sulfone(PPSO) fibers and polyarylsulfone(PASO) fibers were prepared from 2.0 dtex, 51 mm polyphenylene sulfide(PPS) fibers by oxidation modification with hydrogen peroxide as oxidant and glacial acetic acid as catalyst under different oxidation temperatures and reaction time. The morphology and properties of the modified fibers were characterized. The results showed that PPSO fibers were obtained at the oxidation reaction temperature of 25-60 ℃, and PASO fibers were obtained at the oxidation reaction temperature of 80 ℃ under the conditions of hydrogen peroxide-distilled water-glacial acetic acid mass ratio of 50:25:25 and oxidation reaction time 5 h;a large number of oxygen(O) elements appeared in the modified fibers, accompanied by sulfur(S) atom loss and polyaromatic hydrocarbon formation in the process of oxidation modification, which proved that PPS fibers were successfully oxidized;the oxidation treatment had a little effect on the surface morphology of the fibers, but the mechanical properties of the fibers were reduced;after soaking in nitric acid solution, the strength retention rate of PPS fibers was 79.8%, while those of PASO and PPSO fibers were 112.2% and 138.1%, respectively, which indicated that the oxidation resistance of PPS fibers was obviously improved after oxidation modification.

关 键 词：聚苯硫醚纤维 聚苯硫醚砜纤维 聚芳砜纤维 双氧水 氧化处理 抗氧化性 耐高温 

分 类 号：TQ342+.7[化学工程—化纤工业]