65Mn小方坯角部龟裂成因分析及控制  

CAUSE ANALYSIS AND CONTROL OF CORNER CRACKS FOR 65Mn BILLET

在线阅读下载全文

作  者:丁振涛 侯晓林[2] Ding Zhentao;Hou Xiaolin(Longteng Special Steel Co.,Ltd.,Changshu 215511,China;MCC Jingcheng Engineering and Technology Co.,Ltd.,Bejiing 100176,China)

机构地区:[1]常熟市龙腾特种钢有限公司,常熟215511 [2]中冶京诚工程技术有限公司,北京100176

出  处:《冶金信息导刊》2021年第2期18-21,共4页Metallurgical Information Review

摘  要:65Mn钢小方坯角部龟裂对后续轧制影响极大。在分析裂纹成因的基础上,建立了钢水在结晶器中凝固的数学模型。计算结果表明,角部龟裂产生的根本原因是结晶器锥度过大,为方便生产现场管理,应使用旧结晶器铜管浇铸65Mn钢。生产实践表明,该方案解决铸坯角部龟裂的同时,还能有效降低结晶器使用成本。The corner cracks of 65Mn billet have a great influence on the subsequent rolling.Based on the analysis of the causes of cracks,a mathematical model for the solidification of molten steel in the mold was established.The calculation results showed that,the core cause of corner cracks is that the mold taper is too large.In order to facilitate the managementin production,the used mold copper mold should be used for 65Mn casting.Production practice showed that,this proposal can effectively reduce the cost of the moldusing while solving the corner cracks of billet.

关 键 词:65Mn 小方坯 角部龟裂 结晶器锥度 

分 类 号:TF7[冶金工程—钢铁冶金]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象