低盐和低碱活性红染料在柞木单板染色中的应用  

Application of low-alkali and low-salt reactive red dyes in Xylosma japonicum veneer dyeing

作　　者：王敬贤[1] 沈隽[2] 王建军[1] 赫亮[1] 王月婵[1] WANG Jingxian;SHEN Jun;WANG Jianjun;HE Liang;WANG Yuechan(Liaoning Academy of Forestry,Shenyang 110032,Liaoning,China;Engineering Research Center of Advanced Wooden Material,Ministry of Education,Northeast Forestry University,Harbin 150040,Heilongjiang,China)

机构地区：[1]辽宁省林业科学研究院,辽宁沈阳110032 [2]东北林业大学木质新型材料教育部工程研究中心,黑龙江哈尔滨150040

出　　处：《浙江农林大学学报》2021年第3期605-612,共8页Journal of Zhejiang A&F University

基　　金：国家自然科学基金面上项目(31971582);辽宁省农业科学院学科交流合作项目(2020HZ217005)。

摘　　要：【目的】明确低盐和低碱活性染料应用于单板染色的适用性,可降低染液废液污染水平和生产成本。【方法】选择新型低盐活性大红(SNE)染料和低碱活性红(LA)染料对渗透性较差的柞木Xylosma japonicum单板进行染色,以应用较广的活性红(M-3BE)染料作为对照,测试3种染料染色柞木单板的直接性、反应性、固色率和染色效果,利用傅里叶红外光谱(FTIR)、热重分析仪(TG)和扫描电镜(SEM)分析其官能团、组分和细观结构的变化。【结果】与M-3BE染料相比,SNE染料硫酸钠用量降至1/2和LA染料碳酸钠用量降至1/8时,SNE染料固色率提高了15.33%、色差降低了1.35%,LA染料固色率降低了3.37%、色差提高了2.03%。染色处理后,木材表面羟基含量减少,其中低盐染料染色柞木单板羟基含量最低,除出现较弱的硫酸盐S=O吸收峰外,无新吸收峰产生。3种活性染料与木材的结合机理和产生的官能团结构相似,但因染料母体结构差异较大,导致热分解曲线略有不同。染料分子可从木材表面扩散到木材内部,扩散程度从大到小依次为SNE、M-3BE、LA。【结论】SNE染料具有较高的上染率,LA染料具有优异的颜色提升性,可用来染色木材单板,从而降低电解质盐和碱的排放。[Objective] This study is to analyze the applicability of low-alkali and low-salt reactive red dyes in veneer dyeing, with the purpose of reducing the pollution of dyeing wastewater and the cost of production.[Method] A new low-salt reactive red dye(SNE) and low-alkali reactive red dye(LA) were selected to dye Xylosma japonicum veneers with poor permeability. The widely used reactive red dye(M-3 BE) was used as control. The substantivity, reactivity, fixation rate and dyeing effects were tested. Fourier transform infrared spectroscopy(FTIR), thermal gravimetric(TG) analyzer and scanning electron microscopy(SEM) were used to analyze the changes of functional groups, wood components and microstructure of specimens. [Result]Compared with M-3 BE, when the dosages of Na2 SO4 and Na2 CO3 were reduced to 1/2 and 1/8 respectively, the fixation rate of SNE increased by 15.33% and color difference decreased by 1.35%, while the fixation rate of LA decreased by 3.37% and color difference increased by 2.03%. After dyeing, the hydroxyl content on the wood surface decreased, and the lowest hydroxyl content was detected on the X. japonicum wood surface dyedwith SNE dyes. No new absorption peak was observed on the dyed X. japonicum veneers except weak sulfate S=O absorption peak. The mechanism and the functional group structure between three reactive dyes and wood were similar. The thermal decomposition curves were slightly different due to differences in the parent structures of the three reactive dyes. All dye molecules could diffuse to the wood interior from the wood surface, and the order of diffusion degree from large to small was SNE, M-3 BE, and LA. [Conclusion] SNE has high dye uptake and LA has excellent color effect, which can greatly reduce the discharge of electrolyte salt and alkali.

关 键 词：木材学 柞木单板 染色 活性染料 低盐 低碱 

分 类 号：S781.42[农业科学—木材科学与技术]