搅拌器磨损对KR法脱硫搅拌效果的数值分析  

Numerical analysis of the agitator wear on the agitating effect of KR desulfurization

作　　者：龚昌运 但斌斌[1,2] 牛清勇 欧阳德刚 刘洋 闵昌飞 Gong Changyun;Dan Binbin;Niu Qingyong;Ouyang Degang;Liu Yang;Min Changfei(Wuhan University of Science and Technology,Key Laboratory of Metallurgical Equipment and Control Technology,Wuhan 430081,China;Wuhan University of Science and Technology,Hubei Key Laboratory of Mechanical Transmission and Manufacturing Engineering,Wuhan 430081,China;Wuhan Iron and Steel Company Limited,Wuhan 430080,China)

机构地区：[1]武汉科技大学冶金装备及其控制教育部重点实验室,武汉430081 [2]武汉科技大学机械传动与制造工程湖北省重点实验室,武汉430081 [3]武汉钢铁有限公司,武汉430080

出　　处：《材料与冶金学报》2021年第2期97-103,143,共8页Journal of Materials and Metallurgy

基　　金：国家自然科学基金(51475340);湖北省中央引导地方科技发展资金项目(2020ZYYD022);武汉市科技局科技成果转化项目(2019030703011522)。

摘　　要：为探究三叶搅拌器在铁水腐蚀下对铁水搅拌流场的影响,参考传统KR脱硫搅拌工艺过程,利用仿真软件,采用多重参考系法(MRF)及VOF模型,研究了不同磨损程度对三叶搅拌器的搅拌流场与液面状况的影响规律.结果表明:相同搅拌工艺参数条件下,随着搅拌器磨损程度R的增大,搅拌铁水平均流速和平均湍动能降低,搅拌漩涡深度减小,对搅拌流场与液面状况的影响程度逐渐下降;其中,与无磨损(R=0)搅拌器相比,R=15 mm时铁水平均速度减小66.7%,平均湍动能减小82.3%.In order to explore the influence of three-blade agitator on the molten iron flow field under the corrosion environment,a numerical simulation was carried out.The influence law of different wear degrees on the agitated flow field and the liquid level was studied with multiple reference frame method(MRF)and VOF model,comparing with the traditional KR desulfurization agitating process.The results show that the average velocity and the average turbulent kinetic energy of molten iron decrease with the increase of the wear degree R under the same process parameters,the degree of influence on the agitation flow field and the liquid level condition gradually decreases.The depth of agitating vortex also decreases with the increase of the wear degree R.Compared with the agitator without wear(R=0),the average velocity of molten iron decreases by 66.7%and the average turbulent kinetic energy decreases by 82.3%with the wear degree R=15 mm.

关 键 词：搅拌流场 KR脱硫 搅拌器磨损 

分 类 号：TF321.7[冶金工程—冶金机械及自动化]