复杂高硅白合金硫酸氧化浸出工艺及提铜的动力学研究  

Study on process and kinetics of extracting copper from complex high silicon white alloy by sulfuric acid oxidation leaching

作　　者：吴选高 龚傲 喻小强 龙海军 徐志峰[1] 田磊[1] WU Xuan-gao;GONG Ao;CHEN Li-jie;LONG Hai-jun;XU Zhi-feng;TIAN Lei(Institute of Green Metallurgy and Process Intensification,Jiangxi University of Science and Technology,Ganzhou 341000,China)

机构地区：[1]江西理工大学绿色冶金与过程强化研究所,赣州341000

出　　处：《中国有色金属学报》2021年第5期1358-1368,共11页The Chinese Journal of Nonferrous Metals

基　　金：国家自然科学基金资助项目(51804136,51764016);中国博士后科学基金资助项目(2019T120625,2019M652276);江西省自然科学基金资助项目(20181BAB216017);稀有金属分离与综合利用国家重点实验室开放基金资助项目(GK-201803);江西省重点研发计划重点项目(20192ACB70017)

摘　　要：研究了高硅白合金硫酸氧化体系下铜的浸出工艺与动力学。首先采用可控制变量法,通过单因素实验,系统研究了添加剂、硫酸浓度、反应温度、反应时间和液固比对铜钴浸出率的影响,其次通过X射线衍射(XRD)、电感耦合等离子体(ICP)和扫描电镜-能谱(SEM-EDS)对高硅白合金和浸出渣的物相及化学成分进行了分析对比。结果表明:在次氯酸钠用量5 mL、浸出温度343 K、反应时间5 h、硫酸浓度200 g/L、液固比7:1的工艺条件下,铜的浸出率可达99.42%,钴的浸出率可达到97.57%。最后,通过对高硅白合金硫酸氧化浸出提取铜的动力学模型的分析可知,活化能、硫酸浓度和粒度的反应级数分别为34.64 kJ/mol、2.34和0.18,表明其应遵循化学反应控制的收缩核模型,并建立了相应的动力学方程。The leaching process and kinetics of copper in high silicon white alloy sulfuric acid oxidation system were studied.Firstly,the effects of additives,sulfuric acid concentration,reaction temperature,reaction time and liquid-solid ratio on the leaching rate of copper and cobalt were systematically studied by single factor experiment.Secondly,the phase and chemical composition of high silicon white alloy and leaching slag were analyzed by X-ray diffraction(XRD),inductively coupled plasma(ICP)and scanning electron microscopy(SEM-EDS).The results show that the copper and cobalt leaching rate reach 99.42%and 97.57%,respectively,under the conditions of 5 mL in sodium hypochlorite,343 K in leaching temperature,5 h in reaction time,200 g/L in sulfuric acid concentration and 7:1 in liquid-solid ratio.Finally,by analyzing the kinetic model of copper extraction from high silicon white alloy by sulfuric acid oxidation leaching,the activation energy,sulfuric acid concentration and particle size reaction order are 34.64 kJ/mol,2.34 and 0.18,respectively,indicating that it should follow the chemical reaction control of shrinking core model,and establish the corresponding kinetic equation finally.

关 键 词：高硅白合金 硫酸氧化 浸出动力学 混合控制 收缩核模型 

分 类 号：TF813[冶金工程—有色金属冶金]