负离子纤维/竹炭纤维混纺纱及面料开发  

Development ofAnionic Fiber/Bamboo-carbon Fiber Blended Yarn and Fabrics

作　　者：邓燕群 金颖 于丹妮 郭滢[1] 朱军[1] DENG Yan-qun;JIN Ying;YU Dan-ni;GUO Ying;ZHU Jun(School of Textile and Clothing,Nantong University,Nantong 226019)

机构地区：[1]南通大学纺织服装学院,江苏南通226019

出　　处：《纺织科学与工程学报》2022年第1期13-16,21,共5页Journal of Textile Science & Engineering

基　　金：大学生创新训练项目(江苏省重点项目,201910304026Z);内蒙古自治区科技重大专项(ZDZX2018060)。

摘　　要：采用三种不同比例的新型负离子纤维和竹炭纤维混纺,通过正交实验,优选转杯纺纱工艺,并开发针织内衣面料,测试了面料的负离子释放量、吸湿速干性、除臭性能以及力学性能。研究结果表明:原料配比为70/30,针织组织为罗纹半空气层适合做功能性内衣面料。Three different ratios new anionic fibers and bamboo-carbon fibers were used to spin blended yarns,and knitted underwear fabrics were developed by choosing rotor spinning technology and orthogonal experiments.The amount of anion release,moisture absorption and fast drying properties,deodorization and mechanical properties of the fabric were tested.The results showed that when the ratio of the raw materials was 70/30,the rib semi-air layer knitted fabric was suitable for functional underwear fabric.

关 键 词：转杯纺 负离子涤纶纤维 竹炭纤维 除臭性能 力学性能 