LNG储罐用高锰低温钢埋弧焊焊接材料及工艺研究  

Research on Welding Material and Process of High Manganese Low Temperature Steel SAW for LNG Storage Tank

作　　者：陈成 汪昌红 包润新 汪涛 魏艳 张翔 余超 CHEN Cheng;WANG Changhong;BAO Runxin;WANG Tao;WEI Yan;ZHANG Xiang;YU Chao(Wuhan Temo Welding Consumables Co.,Ltd.,Wuhan 430084,China)

机构地区：[1]武汉铁锚焊接材料股份有限公司,湖北武汉430084

出　　处：《电焊机》2023年第5期113-118,共6页Electric Welding Machine

摘　　要：研制出适用于LNG储罐用高锰低温钢配套的埋弧焊丝和焊剂。采用C-Mn-Cr-Ni-Mo合金体系设计,形成的焊缝金属中Mn含量为22.5%~25.5%,焊缝金属抗拉强度和-196℃低温冲击等力学性能优良,与奥氏体高锰低温钢匹配性良好。通过分析道间温度和热输入对熔敷金属力学性能的影响,结果表明,在焊接奥氏体高锰低温钢时,须控制好道间温度和采用较小的热输入,确保焊缝金属具有优良的综合力学性能。The submerged arc welding wire and flux suitable for high manganese cryogenic steel used in LNG storage tank were developed.The C-Mn-Cr-Ni-Mo alloy system was used to design,and the Mn content in the weld metal formed is 22.5%~25.5%.The weld metal has excellent mechanical properties such as tensile strength and-196℃low temperature impact,and has a good match with austenitic high manganese cryogenic steel.By analyzing the influence of inter-pass temperature and heat input on the mechanical properties of deposited metal,the results show that when welding austenitic high manganese cryogenic steel,inter-pass temperature controlled and smaller heat input must be used to ensure that the weld metal has excellent comprehensive mechanical properties.

关 键 词：高锰低温钢 -196℃低温冲击 埋弧焊丝 焊剂 道间温度 

分 类 号：TG423[金属学及工艺—焊接]