CMC-PVA-β-CD三元复合水凝胶的制备  

Preparation of CMC-PVA-β-CD ternary composite hydrogel

作　　者：陈宝定 谢锐邦 黄丽婕[1] 赵含宇 曹畅 彭玉铭 李铭睿 韦应南 Chen Baoding;Xie Ruibang;Huang Lijie;Zhao Hanyu;Cao Chang;Peng Yuming;Li Mingrui;Wei Yingnan(School of Light Industry and Food Engineering,Guangxi University,Nanning 530004,China;School of Light Industry Science and Engineering,South China University of Technology,Guangzhou 510000,China;Guangxi Bossco Environmental Protection Technology Co.,Ltd.,Nanning 530007,China)

机构地区：[1]广西大学轻工与食品工程学院,广西南宁530004 [2]华南理工大学轻工科学与工程学院,广东广州510000 [3]广西博世科环保科技股份有限公司,广西南宁530007

出　　处：《合成树脂及塑料》2024年第1期12-17,共6页China Synthetic Resin and Plastics

基　　金：广西大学“大学生创新创业训练计划”(202210593035);广西大学研究生院博世科分院2020年课题(AA17129006);广西自然科学基金资助(2020GXNSFAA297042);广西清洁化制浆造纸与污染控制重点实验室开放基金(2021KF53)。

摘　　要：以羧甲基纤维素(CMC)、聚乙烯醇(PVA)、β-环糊精(β-CD)为原料,在碱性条件下与环氧氯丙烷(ECH)发生交联反应,制备具有高溶胀性能的CMC-PVA-β-CD三元复合水凝胶,并研究了CMC,PVA,ECH,β-CD添加量对水凝胶溶胀性能、力学性能的影响。结果表明:加入20.0 mL水,0.52 g CMC,0.20 g PVA,1.2 mL ECH,0.24 gβ-CD时,水凝胶溶胀率最高,为2 040.62 g/g,压缩应力为7.90 kPa。与PVA-CMC二元水凝胶相比,CMC-PVA-β-CD三元水凝胶的压缩应力和结晶度均有提高。该三元复合水凝胶具有较高的溶胀率和良好的力学性能,在生物医药、消毒杀菌领域具有很高的应用价值。Carboxymethyl cellulose(CMC),polyvinyl alcohol(PVA)andβ-cyclodextrin(β-CD)were used as raw materials to prepare CMC-PVA-β-CD ternary composite hydrogel with high swelling properties via crosslinking reaction with epichlorohydrin(ECH)under alkaline conditions.The influence of additions of CMC,PVA,ECH andβ-CD on swelling properties and mechanical properties of the gel were investigated.The results show that when 20 mL of water,0.52 g of CMC,0.20 g of PVA,1.2 mL of ECH,0.24 g ofβ-CD are added,the swelling rate of the hydro gel is the highest of 2040.62 g/g and the compressive stress is 7.90 kPa.The compressive stress and crystallinity of the CMC-PVA-β-CD ternary gel are higher than those of the PVA-CMC binary gel.The hydrogel prepared has high swelling rate and excellent mechanical properties,wihich is valuable in biomedicine,disinfection and sterilization.

关 键 词：水凝胶 溶胀率 聚乙烯醇 羧甲基纤维素 Β-环糊精 