导电二氧化钛制备工艺研究及在导电涂料中的应用  

A Study on the Conductive Titanium Dioxide Preparation Process and the Application in Conductive Coatings

作　　者：任健 REN jian(CITIC Titanium Industry Co.,Ltd.,Jinzhou 121011,Liaoning,China)

机构地区：[1]中信钛业股份有限公司,辽宁锦州121011

出　　处：《中国涂料》2024年第2期58-61,共4页China Coatings

摘　　要：针对导电二氧化钛的应用要求,在金红石型二氧化钛浆料的基础上,表面包覆一层ATO(SnO_(2)掺杂Sb_(2)O_(3)),制备ATO/TiO_(2)复合粉体。以粉体体积电阻率作为评价指标,考察包膜的pH值、温度以及包膜剂放入的时间、五水氯化锡的加入量、m(SbCl_(3))/m(SnCl_(4)·5H_(2)O)及煅烧温度等制备工艺,并对导电机理进行了研究。实验得出较佳的制备条件:pH值为2、包膜温度60℃、加料时间3 h、w(SnCl_(4)·5H_(2)O)为60%、m(SbCl_(3))/m(SnCl_(4)·5H_(2)O)=0.1、煅烧温度600℃。金红石型二氧化钛浆料中加入ATO(SnO_(2)掺杂Sb_(2)O_(3)),可克服产生静电的现象。同时有非常好的耐受性和导电性,助力功能型工业涂料的快速发展。According to the performance requirements of conductive titanium dioxide and on the basis of rutile titanium dioxide slurry,a layer of ATO(SnO_(2)doped Sb_(2)O_(3))was coated on the surface of titanium dioxide for preparation of ATO/TiO_(2)composite powder.Taking the volume resistivity index of the powder as the evaluation index,the preparation processes such as coating pH value,coating temperature,coating agent addition time,w(SnCl_(4)·5H_(2)O),m(SbCl_(3))/m(SnCl_(4)·5H_(2)O)and calcination temperature were investigated,and the conductive mechanism was also studied.Better preparation conditions were obtained by experiments:pH=2,coating temperature is 60℃,the feeding time is 3 h,w(SnCl_(4)·5H_(2)O)=60%,m(SbCl_(3))/m(SnCl_(4)·5H_(2)O)=0.1,calcination temperature is 600℃.ATO(SnO_(2)doped Sb_(2)O_(3))was added into rutile titanium dioxide slurry to overcome the phenomenon of static electricity.At the same time,it has very good tolerance and conductivity,supporting the rapid development of functional industrial coatings.

关 键 词：二氧化钛 ATO 粉体电阻率 煅烧温度 

分 类 号：TQ630.49[化学工程—精细化工]