碳化法制备高比表面积纳米白炭黑的工艺条件研究  

Study on the process conditions for the preparation of nano silica with high specific surface area by carbonization method

作　　者：张少奇 杨保俊 王琦 王朋辉 王百年 ZHANG Shao-qi;YANG Bao-jun;WANG Qi;WANG Peng-hui;WANG Bai-nian(School of Chemistry and Chemical Engineering,Hefei University of Technology,Hefei 230009,China)

机构地区：[1]合肥工业大学化学与化工学院

出　　处：《应用化工》2024年第4期853-857,共5页Applied Chemical Industry

基　　金：安徽省科技重大专项(112175456041)。

摘　　要：以工业水玻璃为原料,CO_(2)为沉淀剂,着重开展碳化法制备纳米白炭黑的碳化反应过程工艺条件研究。以所制备纳米白炭黑样品的平均粒径、BET值为主要考察指标,筛选并确定较适宜的复配分散剂为2%TTLY+1%TTLX;考察并确定较适宜的碳化反应工艺条件为:体系SiO_(2)质量浓度11%,碳化反应温度60℃,水玻璃模数3.3,Na_(2)CO_(3)初始含量3%;所制备出的纳米白炭黑样品平均粒径为23.43 nm,BET值达到422.77 m^(2)/g,样品为无定形非晶态结构,粒度均匀性和分散性均较好。Industrial water glass was used as raw material and CO_(2) as precipitant,focusing on the research on the process conditions of carbonization reaction to prepare nano silica by carbonization.The average particle size and BET values of the prepared nano silica samples were taken as the main investigation indexes.2%TTLY+1%TTLX was screened and determined as the more suitable compound dispersant;and the carbonization condition was optimized as:the mass concentration of SiO_(2) 11%,the temperature of carbonization reaction 60 ℃,the modulus of water glass 3.3,and the initial content of Na_(2)CO_(3) 3%.The average particle size of the prepared nano silica sample was 23.43 nm,the BET values reached 422.77 m^(2)/g,and the sample was an amorphous structure,with good particle size uniformity and dispersion.

关 键 词：碳化法 纳米白炭黑 粒径 BET 

分 类 号：TQ127.2[化学工程—无机化工] TQ177.4