QY9611双马来酰亚胺树脂流变性能研究  

Rheological properties of QY9611 bismaleimide resin

作　　者：张文君 王成 王亚敏 ZHANG Wenjun;WANG Cheng;WANG Yamin(Anhui Jialiqi Advanced Composite Material Technology Co.,Ltd.,Suzhou 234000)

机构地区：[1]安徽佳力奇先进复合材料科技股份公司,宿州234000

出　　处：《纤维复合材料》2025年第1期53-56,共4页Fiber Composites

摘　　要：利用差示扫描量热仪(DSC)升温测试,得到QY9611树脂体系的固化特性,利用旋转流变仪对QY9611树脂体系进行升温流变测试,得到QY9611树脂体系的黏度—温度曲线,进一步对QY9611数值体系进行恒温测试,可得到树脂体系不同时间黏度—时间曲线,通过阿伦尼乌兹方程进行拟合得到了QY9611树脂体系的流变模型。研究结果为QY9611树脂复合材料的成型加工提供了理论依据和实验数据参考。The curing characteristics of QY9611 resin system were obtiaine through temperature-rise using DSC,Rheological tests on the QY9611 resin system were conducted with a rotational rheometer to derive the viscosity-temperature curve.Further isothermal tests on the QY9611 resin system yielded viscosity-time curves at different times.The rheological model of the QY9611 resin system was obtained by fitting the date with the Arrhenius equation.The research results provide theoretical basis and experimental date reference for the molding and processing of QY9611 resin composite materials.

关 键 词：QY9611树脂 流变模型 固化特性 黏度 

分 类 号：TQ3[化学工程]