GI-Ⅱ型渗透陶瓷氧化铝粉浆粘度的测试  

Determination or alumina slurry viscosity of GI-Ⅱ infiltrated ceramic

作　　者：王航[1] 巢永烈[1] 廖运茂[1] 巢齐宇[1] 高卫民[1] 

机构地区：[1]四川大学华西口腔医学院,讲师硕士四川610041

出　　处：《口腔颌面修复学杂志》2001年第1期45-46,共2页Chinese Journal of Prosthodontics

基　　金：四川省卫生厅科研资助项目 编号:970106

摘　　要：目的：测试ＧＩ－Ⅱ型渗透陶瓷氧化铝粉浆粘度，探讨在涂塑中的注意事项。材料与方法：将氧化铝粉体及其专用调和液分别按粉液质量比８：１，７：１，６：１，５：１，４：１的比例配制２份，其中１份加入增塑剂，用旋转法测粘度。结果：粉液比越小，粘度越大；粉液比为７、６、５、４时，粘度变化相对缓慢；粉浆中加入增塑剂，可以明显降低粘度；粉浆粘度随剪切速率增大而减小。结论：调拌粉浆时可选择４～７：１粉液比及加入增塑剂。同时，应充分超声振荡，以有利于粉浆中粉体分散均匀和排除气泡。Objective: This study was to determine alumina slurry viscosity of GI-Ⅱ Infiltrated Ceramic for complications of its slip casting. Methods: The Two alumina slurries with powder-to-mixing liquid mass ratio of 8: 1, 7: 1, 6: 1, 5: 1, 4: 1, respectively,one of which was added plasticizer, were prepared. Their viscosity values were determined with rotation method. Results: The viscosity values declined along with powder/liquid ratios and rose with shear rate. The values changed much more slowly when powder/liquid ratios were 8: 1,7: 1,6: 1,5: 1,4: 1,respectively. And addition of the plasticizer into the slurries significantly reduced their viscosity values. Conclusions: It may be advisable to choose powder/liquid ratios of 7～4:1 and add plasticzer into alumina slurry before slip casting, while with enough ultrasonic vibration in order to distribute powder evenly in the slurry and remove possible air bubbles.

关 键 词：GI-II型渗透陶瓷 氧化铝 粘度 测试 牙科 涂塑 

分 类 号：R783.1[医药卫生—口腔医学]