合成条件对高温高压条件下制备CrO₂晶体的影响  

The Influence of Synthesis Conditions on the Fabrication of CrO2 Crystals under High Temperature and High Pressure Conditions

作　　者：黄培钊 刘毅 李京城 金怡珑 周志湘 李瑞[2] 丁龙[3] 黄海亮 

机构地区：[1]牡丹江师范学院物理与电子工程学院,黑龙江 牡丹江 [2]齐齐哈尔大学理学院,黑龙江 齐齐哈尔 [3]齐齐哈尔大学教师教育学院,黑龙江 齐齐哈尔

出　　处：《材料科学》2024年第11期1647-1653,共7页Material Sciences

摘　　要：采用高纯度的Cr2O5作为原料,利用高温高压方法在不同合成条件下制备高纯度的CrO2,研究不同的合成条件对于制备CrO2晶粒尺寸和形貌的影响。结果表明:随着合成温度的降低,晶粒尺寸明显减小;合成压力的升高,晶粒尺寸明显减小,完整度有一定的提高,但晶体长径比减小;合成时间的变化对晶粒尺寸和晶型完整度无明显影响。High-purity CrO2 was prepared using high-purity Cr2O5 as the raw material through a high temperature and high pressure (HTHP) method under various synthesis conditions. The influence of different synthesis conditions on the grain size and morphology of the prepared CrO2 was investigated. The results indicate that as the synthesis temperature decreases, the grain size decreases significantly. With an increase in synthesis pressure, the grain size also decreases markedly, and the crystallinity improves to some extent, although the aspect ratio of the crystals diminishes. Changes in synthesis time have no notable effect on grain size or crystallinity.

关 键 词：CrO₂ 高温高压 合成工艺 晶体形貌 

分 类 号：O62[理学—有机化学]