Effect of Some Plating Variables on Zinc Coated Low Carbon Steel Substrates  

作　　者：Bamidele M. Durodola Joseph A.O. Olugbuyiro 

机构地区：[1]Department of Chemistry, College of Science and Technology Covenant University, Ota, Ogun state, Nigeria

出　　处：《Journal of Minerals and Materials Characterization and Engineering》2011年第13期1255-1262,共8页矿物质和材料特性和工程（英文）

摘　　要：This work examined the effect of plating variables on zinc coated low carbon steel substrates. The electrodeposition of steel substrates was carried out in zinc electrolyte bath. Time, voltage, distance from the anode to the cathode and the immersion depth served as plating variables. The results showed that weight gained increases as the plating time increases for the constant depth of immersion while the weight gained per unit time by varying immersion depth is irregular. Also, the study demonstrated that sample plated for 20 minutes;20cm from the anode, 45cm depth of immersion at 0.8V exhibited the best plating properties with homogeneity of diffuse plating efficiency.This work examined the effect of plating variables on zinc coated low carbon steel substrates. The electrodeposition of steel substrates was carried out in zinc electrolyte bath. Time, voltage, distance from the anode to the cathode and the immersion depth served as plating variables. The results showed that weight gained increases as the plating time increases for the constant depth of immersion while the weight gained per unit time by varying immersion depth is irregular. Also, the study demonstrated that sample plated for 20 minutes;20cm from the anode, 45cm depth of immersion at 0.8V exhibited the best plating properties with homogeneity of diffuse plating efficiency.

关 键 词：VARIABLES Zinc-coated low carbon steel SUBSTRATES Depth of IMMERSION Electrodeposition 

分 类 号：R73[医药卫生—肿瘤]