Effect of Thermoplastic Incorporation on the Performance of Thermosetting Matrix  

作　　者：R. Ollier A. Stocchi E. Rodriguez V. Alvarez 

机构地区：[1]Materials Science and Technology Research Institute (INTEMA) University of Mar del Plata - National Research Council (CONICET), Av. Juan B. Justo 4302 - B7608FDQ - Mar del Plata, ARGENTINA

出　　处：《Materials Sciences and Applications》2012年第7期442-447,共6页材料科学与应用期刊（英文）

摘　　要：In this work, the morphology, thermal and viscoelastic properties, deformation and fracture behaviour of a commercial vinylester resin modified with a biodegradable polymer was investigated. Flexural, impact and fracture tests were per-formed on the blends with different polycaprolactone (PCL) contents. They exhibited improved stiffness and fracture properties in comparison to the neat resin. From SEM analysis of fracture surfaces, stress whitening and branced frac-ture paths toughening mechanisms were identified. The dependence of the glass transition temperature with PCL con-tent was adequately fitted by simple models available in the literature. From the results of these models along with the results of calorimetric studies and SEM analysis, it can be concluded that the interaction between vinylester and PCL is strong enough to avoid phase separation.In this work, the morphology, thermal and viscoelastic properties, deformation and fracture behaviour of a commercial vinylester resin modified with a biodegradable polymer was investigated. Flexural, impact and fracture tests were per-formed on the blends with different polycaprolactone (PCL) contents. They exhibited improved stiffness and fracture properties in comparison to the neat resin. From SEM analysis of fracture surfaces, stress whitening and branced frac-ture paths toughening mechanisms were identified. The dependence of the glass transition temperature with PCL con-tent was adequately fitted by simple models available in the literature. From the results of these models along with the results of calorimetric studies and SEM analysis, it can be concluded that the interaction between vinylester and PCL is strong enough to avoid phase separation.

关 键 词：POLYMER MATRIX COMPOSITES Mechanical Properties FRACTURE 

分 类 号：R73[医药卫生—肿瘤]