Physico-Mechanical Properties of Luffa aegyptiaca Fiber Reinforced Polymer Matrix Composite  

作　　者：S. I. Ichetaonye I. C. Madufor M. E. Yibowei D. N. Ichetaonye 

机构地区：[1]Department of Polymer and Textile Technology, Yaba College of Technology, Yaba, Lagos, Nigeria [2]Department of Polymer and Textile Engineering, Federal University of Technology, Owerri, Nigeria

出　　处：《Open Journal of Composite Materials》2015年第4期110-117,共8页复合材料期刊（英文）

摘　　要：This paper presents the study of moisture content, hardness, bulk density, apparent porosity, tensile and flexural characteristics of composite properties of Luffa aegyptiaca fiber. Luffa aegyptiaca reinforced epoxy composites have been developed by hand lay-up method with Luffa fiber untreated and treated conditions for 12 Hrs and 24 Hrs in different filler loading as in 2:1 ratio (5%, 10%, 15%, 20% and 25%). The effects of filler loading on the moisture content, hardness, bulk density, apparent porosity, tensile and flexural properties were studied. In general, the treated Luffa fibre composite for 24 Hrs showed better improvement properties via addition of modified Luffa fibre as reinforcement. However, tensile and flexural properties improved continuously with increasing filler loading up to 20% but decreasing at 25% due to weak interfacial bonding for both untreated and treated composite. The favourable results were obtained at 20% for treated composite at 24 Hrs especially at tensile and flexural characteristics and are suitable for mechanical applications.This paper presents the study of moisture content, hardness, bulk density, apparent porosity, tensile and flexural characteristics of composite properties of Luffa aegyptiaca fiber. Luffa aegyptiaca reinforced epoxy composites have been developed by hand lay-up method with Luffa fiber untreated and treated conditions for 12 Hrs and 24 Hrs in different filler loading as in 2:1 ratio (5%, 10%, 15%, 20% and 25%). The effects of filler loading on the moisture content, hardness, bulk density, apparent porosity, tensile and flexural properties were studied. In general, the treated Luffa fibre composite for 24 Hrs showed better improvement properties via addition of modified Luffa fibre as reinforcement. However, tensile and flexural properties improved continuously with increasing filler loading up to 20% but decreasing at 25% due to weak interfacial bonding for both untreated and treated composite. The favourable results were obtained at 20% for treated composite at 24 Hrs especially at tensile and flexural characteristics and are suitable for mechanical applications.

关 键 词：LUFFA aegyptiaca FIBER FLEXURAL FILLER LOADING 

分 类 号：R73[医药卫生—肿瘤]