Experimental Investigation on the Properties of Recycled Concrete Using Hybrid Fibers  

作　　者：Salim Khoso Janet Raad Azadeh Parvin 

机构地区：[1]Department of Civil and Environmental Engineering, The University of Toledo, Toledo, OH, USA

出　　处：《Open Journal of Composite Materials》2019年第2期183-196,共14页复合材料期刊（英文）

摘　　要：Due to the inherent property of concrete being very weak in tension, efforts have been made to overcome this deficiency by adding various type of fibers like carbon fiber reinforced polymer (CFRP), glass fiber reinforced polymer (GFRP), polypropylene fiber (PPF) and stainlesssteel fiber (SSF) smeared into the concrete mix. The present study involves experimental investigation on the use of GFRP, CFRP and SSF fibers alone or as combination to improve the mechanical properties of concrete. Furthermore, concrete cylinders were cast and tested for compression and tension using 10% fly ash as cement replacement in all specimens. Besides fiber material types, fiber reinforcement ratios of 1% and 1.5% were tested to investigate the mechanical properties of concrete. In all concrete cylinder tests, the fiber reinforcement ratio of 1% had a significant contribution in increasing the tensile strength as oppose to compressive strength. As a result, the tensile and compressive strengths were increased by 26% and 11%, respectively as compared to the control specimen. Increasing the fiber reinforcement ratio from 1% to 1.5%, resulted in diminishing the mechanical properties of concrete. However, reduction in concrete compressive strength was more prominent than the tensile strength. Furthermore, it was observed that, the crack propagation was decreased with the increase of fiber content when compared to the control specimen.Due to the inherent property of concrete being very weak in tension, efforts have been made to overcome this deficiency by adding various type of fibers like carbon fiber reinforced polymer (CFRP), glass fiber reinforced polymer (GFRP), polypropylene fiber (PPF) and stainlesssteel fiber (SSF) smeared into the concrete mix. The present study involves experimental investigation on the use of GFRP, CFRP and SSF fibers alone or as combination to improve the mechanical properties of concrete. Furthermore, concrete cylinders were cast and tested for compression and tension using 10% fly ash as cement replacement in all specimens. Besides fiber material types, fiber reinforcement ratios of 1% and 1.5% were tested to investigate the mechanical properties of concrete. In all concrete cylinder tests, the fiber reinforcement ratio of 1% had a significant contribution in increasing the tensile strength as oppose to compressive strength. As a result, the tensile and compressive strengths were increased by 26% and 11%, respectively as compared to the control specimen. Increasing the fiber reinforcement ratio from 1% to 1.5%, resulted in diminishing the mechanical properties of concrete. However, reduction in concrete compressive strength was more prominent than the tensile strength. Furthermore, it was observed that, the crack propagation was decreased with the increase of fiber content when compared to the control specimen.

关 键 词：Fiber-Reinforced Concrete FLY-ASH COMPRESSIVE STRENGTH TENSILE STRENGTH Carbon FIBER Glass FIBER STAINLESS Steel FIBER 

分 类 号：R73[医药卫生—肿瘤]