纳米微晶SnO_2薄膜的制备和光学性能的研究  

Preparation of Nanocrystalline SnO_2 Thin Films and Researchon Its Optical Characteristics

作　　者：林殷茵[1] 刘秦[1] 杨合情[1] 张良莹[1] 姚熹[1] 

机构地区：[1]西安交通大学电子材料与器件研究所

出　　处：《压电与声光》1998年第4期263-266,共4页Piezoelectrics & Acoustooptics

摘　　要：以无机盐为原料制备得到纳米微晶ＳｎＯ２薄膜。由透射比曲线计算发现，随热处理温度的升高，薄膜的折射率、消光系数均增大。研究表明，掺Ｔｉ的ＳｎＯ２薄膜吸收边的跃迁属间接跃迁，随晶粒尺寸的减小，间接带宽增大。Nanocrystalline　SnO_2　thin　films　was　prepared　from　inorganic　salt.According　to　calculation　of　the　transmittance　curve,it　was　found　that　refractive　index　and　extinction　coefficient　of　the　thin　films　increased　with　decreasement　of　the　heating　temperature.As　a　showing　of　research　work,the　absorption　edge　of　Ti　doped　SnO_2　thin　films　was　attributable　to　indirect　transition.The　band　gap　of　the　films　increased　with　decreasing　grain　size.

关 键 词：二氧化锡 纳米微晶 间接跃迁 吸收边 导电材料 

分 类 号：TN304.21[电子电信—物理电子学] TM240.143[一般工业技术—材料科学与工程]