慢正电子束研究质子辐照CLAM钢产生的缺陷及其退火行为  

Proton irradiation defects in CLAM steel and their annealing behavior studied by slow positron beams

作　　者：章征柏[1] 叶邦角[1] 翁惠民[1] 彭蕾[2] 刘建党[1] 楼捷[1] FDS团队 

机构地区：[1]中国科学技术大学近代物理系,安徽合肥230026 [2]中国科学院等离子体物理研究所,安徽合肥230031

出　　处：《核科学与工程》2009年第3期273-277,共5页Nuclear Science and Engineering

基　　金：国家自然科学基金资助项目(10675114;10675115)

摘　　要：为了研究中国低活化马氏体CLAM钢的辐照损伤机理,本文利用慢正电子技术研究了质子辐照CLAM钢时所产生的缺陷及其退火回复行为,发现辐照在材料中产生空位团数密度随质子注量增加而增多,而其尺度增大并不明显。辐照仅产生原子尺度的空位和空位团,400℃退火可以使缺陷很好地消除。此外分析了硅对CLAM钢辐照性能的影响,实验上没有观察到硅的添加抑制了质子辐照缺陷的产生。In order to investigate radiation damage mechanism of the China low activation martensitic （CLAM） steel, the proton radiation damage of CLAM steel and the annealing behavior of defect were probed by slow positron beam. It was found that the density of vacancies increased, and the size reached a saturation value, with increasing of irradiation fluence. The whole region of irradiated sample was only slightly damaged. Small vacancies and vacancy clusters were the dominant defects, and were recovered after annealing at 400 ℃. Besides, the effect of minor additive Si on irradiation behavior for CLAM steel was studied. The experimental results showed that additive Si can not prevent proton irradiation defects.

关 键 词：质子辐照 缺陷 慢正电子 CLAM钢 

分 类 号：TL64[核科学技术—核技术及应用]