低温烧结BaO-TiO_2-ZnO系陶瓷的研究  

Study on BaO-TiO_2-ZnO system ceramics sintered at low temperature

作　　者：黄刚[1] 吴顺华[1] 张宝林[1] 李世春[1] 王新[1] 

机构地区：[1]天津大学电子信息工程学院,天津300072

出　　处：《电子元件与材料》2010年第12期52-55,共4页Electronic Components And Materials

摘　　要：将ZnO-H3BO3(ZB)玻璃作为烧结助剂添加到BaO-TiO2-ZnO系(BTZ)陶瓷中,以实现BTZ陶瓷的低温烧结。研究了ZB玻璃的加入及球磨时间对BTZ陶瓷的烧结性能和介电性能的影响。结果表明:ZB玻璃的加入,明显降低了BTZ陶瓷的烧结温度。添加质量分数6%的ZB玻璃、球磨10 h时,BTZ陶瓷能够在950℃下致密烧结,获得良好的介电性能(1 MHz):εr=35.55,tanδ=2.2×10–4,–10×10–6/℃<α<+10×10–6/℃(–55～+125℃)。ZnO-H3BO3（ZB） glass（as sintering aid） was added to lower the sintering temperature of BaO-TiO2-ZnO system（BTZ） ceramics.The effects of addition of ZB glass and milling time on the sinterability and the dielectric properties of BTZ ceramics were investigated.The results show that sintering temperature of the BTZ ceramics is decreased obviously with the addition of ZB.The BTZ ceramics which doped with 6%（mass fraction） ZB glass and milled for 10 h,are densely sintered at 950 ℃ with good dielectric properties（at 1 MHz）： εr=35.55,tanδ = 2.2×10^–4,–10×10^–6/℃α＋10×10^–6/℃（–55～＋125 ℃）.

关 键 词：BaO-TiO2-ZnO LTCC 球磨时间 介电性能 

分 类 号：TM28[一般工业技术—材料科学与工程]