高纯Al-0.5%Cu合金的轧制织构  

Rolling Texture of High Purity Al-0.5%Cu Alloy

作　　者：万小勇[1] 江轩[1] 王欣平[1] 程明[1] 朱晓光[1] 

机构地区：[1]北京有色金属研究总院北京有研亿金新材料股份有限公司,北京100088

出　　处：《有色金属》2011年第2期6-9,共4页Nonferrous Metals

摘　　要：采用取向分布函数(ODF)研究轧制形变量对高纯A l-0.5%Cu合金织构的影响。结果表明,30%轧制变形量主要有{112}<351>,50%时{114}<110>织构,70%时出现了较强的铜式织构{211}<111>和{111}纤维织构,在形变量达到90%后,由于出现了剪切力,织构为非常强烈的旋转立方{001}<110>。分析A l-0.5%Cu合金的α和β线,发现随着变形量的增大,织构向C取向聚集。The deformation textures of high purity Al-0.5%Cu alloy are investigated by means of orientation distribution functions（ODFs）.The results show that the main deformation textures of reduction 30% and 50% are {112}351 and {114}110,the reduction 70% alloy is mainly composed of strong C{211}111 and small {111}fiber texture.When the cold rolling reduction is approximately 90%,the textures becomes to very strong R-cube{001}110 because of shear stress.During the rolling of Al-0.5%Cu alloy,the C{211}111 is the stable texture in the α fibre and β fibre.

关 键 词：金属材料 Al-0.5%Cu合金 轧制变形 取向 织构 

分 类 号：TG146.21[一般工业技术—材料科学与工程] TG113.12[金属学及工艺—金属材料]