预注入对Si_(1-x)C_x合金形成的影响  

THE EFFECTS OF PRE-IRRADIATION ON THE FORMATION OF Si_(1-x)C_x ALLOYS

作　　者：王引书[1] 李晋闽[2] 王衍斌[3] 王玉田[2] 孙国胜[2] 林兰英[2] 

机构地区：[1]北京师范大学物理系,北京100875 [2]中国科学院半导体研究所,北京100083 [3]中国科学院近代物理研究所,兰州730000

出　　处：《物理学报》2001年第7期1329-1333,共5页Acta Physica Sinica

摘　　要：室温下在单晶Si中注入 (0 6— 1 5 )at%的C原子 ,部分样品在C离子注入之前在其中注入2 9Si+ 离子产生损伤 ,然后在相同条件下利用高温退火固相外延了Si1 -xCx 合金 ,研究了预注入对Si1 -xCx 合金形成的影响 .如果注入C离子的剂量小于引起Si非晶化的剂量 ,在 95 0℃退火过程中注入产生的损伤缺陷容易与C原子结合形成缺陷团簇 ,难于形成Si1 -xCx 合金 ,预注入形成的损伤有利于合金的形成 .随着C离子剂量的增大 ,注入产生的损伤增强 ,预注入反而不利于Si1 -xCx 合金的形成 ,但当注入C原子的浓度超过固相外延的溶解度时 ,预注入的影响可以忽略 .退火温度升高到 10 5 0℃ ,无论预注入还是未预注入样品 ,C含量低的合金相仍然保留 ,而C含量高的合金相大部分消失 .Carbon ions were implanted into crystal Si to a concentration of (0.6-1.5)at% at room temperature. Some samples were pre-irradiated with S-29(i)+ ions, while others were not pre-irradiated. Then the two kinds of samples were implanted with C-12(+) ions simultaneously, and Si1-xCx alloys were grown by solid phase epitaxy with high-temperature annealing. The effects of preirradiation on the formation of Si1-xCx alloys were studied. If the dose of implanted C ion was less than that for amorphizing Si crystals, the implanted C atoms would like to combine with defects produced during implantation, and then it was difficult for Si1-xCx alloys to form after annealine, at 950 degreesC. Pre-irradiation was advantageous for Si1-xCx alloy formation. With the increase of C ion dose, the damage produced by C ions increased. Pre-irradiation was unfavorable for Si1-xCx, alloy formation. If the implanted C concentration was higher than that for solid phase epitaxy solution, only part of the implanted C atoms form Si1-xCx alloys and the effects of pre-irradiation could be neglected. As the annealing temperature was increased to 1050 degreesC, Si1-xCx alloys in both pre-irradiated and unpreirradiated samples of low C concentration remained, whereas most part of Si1-xCx alloys in samples with high C concentration vanished.

关 键 词：离子注入 固相外延 Si1-xCx合金 损伤 形成机理 

分 类 号：TG13[一般工业技术—材料科学与工程]