低成本羧甲基纤维素水凝胶制备及其吸附性能探索型实验设计  

Experimental design for the preparation of low-cost carboxymethylcellulose hydrogel and its adsorption performance

作　　者：包月平 Ganesh Kumar 胡晓 展思辉[1] 张贺 BAO Yueping;GANESH Kumar;HU Xiao;ZHAN Sihui;ZHANG He(College of Environmental Science and Engineering,Nankai University,Tianjin 300350,China;School of Materials Science and Engineering,Nanyang Technological University,Singapore 639798,Singapore)

机构地区：[1]南开大学环境科学与工程学院,天津300350 [2]南洋理工大学材料科学与工程学院,新加坡639798

出　　处：《实验技术与管理》2024年第2期81-89,共9页Experimental Technology and Management

基　　金：南开大学中央高校基本科研业务费专项资金项目(63231132,63231195)。

摘　　要：羧甲基纤维素水凝胶分子内含有大量的羧基和羟基官能团,能够高效吸附水体中的有机污染物,同时由于水凝胶的易回收和生物相容性,目前已被广泛应用于印染废水处理。但传统的羧甲基纤维素水凝胶制备方法存在耗时长、成本高、污染重等问题。该实验设计结合我国资源化发展和环境保护需要,以纤维素水凝胶为原料,以水代替部分传统有机溶剂,开发出一种室温下快速制备羧甲基纤维素水凝胶的绿色合成方案。合成时间从44 h缩短至约4h,制备成本降低约95%,同时减少了化学试剂的使用,避免了二次污染。实验选用典型染料亚甲基蓝作为模型污染物,考察了羧甲基纤维素水凝胶对其在不同水体环境中的吸附性能。[Objective]Carboxymethylcellulose hydrogels,rich in carboxyl and hydroxyl functional groups,are effective in adsorbing organic pollutants in water and wastewater.Their wide application in the treatment of printing and dyeing wastewater in China is attributed to their high biocompatibility and ease of recovery.However,the traditional process for preparing these hydrogels has shortcomings,such as being time-consuming,costly,and causing secondary pollution.[Methods]In line with the government’s commitment to resource development and environmental protection,we propose a room-temperature,rapid green synthesis process for carboxymethylcellulose hydrogel.This method uses cellulose hydrogel instead of cellulose powder as the raw material and partially replaces the organic solvent with water.This novel green method allows for a high degree of substitution on the hydrogel surface owing to the insolubility of raw cellulose hydrogels.Additionally,the COO–functional groups can be retained on the hydrogels because there was no need for acidification.This process is also more time-efficient owing to its simplicity compared to traditional one-pot synthesis methods.Typically,our preparation procedure consists of three steps:alkaline activation,crosslinking,and carboxymethyl conversion.This simplifies the process significantly compared to traditional methods.We began by optimizing various parameters that affect the synthesis of carboxymethylcellulose hydrogels,such as reaction solvent,activation time,crosslinker amount,crosslinking time,conversion time,and final drying method.[Results]Based on characterizations reflecting the morphologies and surface functional groups of the as-prepared carboxymethylcellulose hydrogels,we established an optimized synthesis process.In this process,the reaction medium was set as isopropyl alcohol/water at 1:1(v/v),the NaOH activation time was 40 min,the crosslinking time was 20 min with a crosslinker amount of 1.0 mL,the conversion time was 3 h,and the final drying method was freeze-drying.The

关 键 词：羧甲基纤维素 水凝胶 亚甲基蓝 吸附 