半绝缘砷化镓中本征缺陷的光学显微研究  被引量:2

Investigation of the native defects in LEC SI-GaAs by optical microscopy

在线阅读下载全文

作  者:刘红艳[1] 孙卫忠[1] 王娜[1] 郝秋艳[1] 刘彩池[1] 

机构地区:[1]河北工业大学信息功能材料研究所,天津300130

出  处:《现代仪器》2008年第3期38-40,共3页Modern Instruments

基  金:河北省科学技术研究与发展指导计划和河北工业大学博士启动基金(07215138)

摘  要:本文利用光学显微技术系统分析热处理对液封直拉法生长的半绝缘砷化镓(LECSI-GaAs)中本征缺陷的影响。实验结果表明,晶体生长后的热处理可以影响砷沉淀的密度与分布。500℃热处理对As沉淀的密度无明显影响;真空条件下,在850-930℃范围内热处理AB腐蚀坑变浅,砷沉淀数量增加;真空条件下,高于1100℃热处理后,砷沉淀几乎消失。晶体中砷沉淀的密度会随热处理条件的不同而变化,本文对其机理进行探讨。The effects of thermal annealing on the native defects in LEC SI-GaAs were studied by optical microscopy. The results showed that the thermal annealing could affect the density and distribution of the arsenic precipitates. The density and distribution of the arsenic precipitates can not be affected obviously at 500 ℃, Under vacuum conditions, AB etching pits become shallower, and the number of arsenic precipitates increases in the range of the 850-930 ℃. Under vacuum conditions, arsenic precipitates almost disappear after thermal annealing above 1100℃. The density of arsenic precipitates in SI-GaAs crystal changes with different thermal annealing conditions, the mechanism of the change was discussed.

关 键 词:半绝缘砷化镓 热处理 砷沉淀 光学显微技术 

分 类 号:TN304.23[电子电信—物理电子学] TU528.45[建筑科学—建筑技术科学]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象