超临界二氧化碳注入法制备α生育酚/介孔二氧化硅复合物  

Preparation of α-tocopherol/mesoporous silica complex using supercritical carbon dioxide impregnation method

作　　者：忻娜[1] 沈佩琼[1] 王燕[1] 赵亚平[1] 

机构地区：[1]上海交通大学化学化工学院,上海200240

出　　处：《食品工业科技》2012年第15期194-197,共4页Science and Technology of Food Industry

基　　金：国家自然科学基金项目(20976103)

摘　　要：以介孔二氧化硅为载体,α-生育酚为负载物,研究了超临界二氧化碳注入法制备α-生育酚/介孔二氧化硅复合物的工艺,分析和表征了复合物的结构,考察了注入压力、温度和时间对α-生育酚负载量的影响。结果表明:当注入时间一定时,α-生育酚的负载量随温度和压力的升高先增加后减少;当温度为35℃,压力为18MPa,注入时间为1h时,α-生育酚的负载量达到76.14%。The mesoporous silica loaded with α-tocopherol was prepared using supercritical carbon dioxide impregnation technology.The complex of α-tocopherol and mesoporous silica was characterized.The effect of pressure,temperature and reaction time on α-tocopherol loading was studied.The results showed that α-tocopherol loading increased first and then decreased with increasing pressure and temperature at the constant of reaction time.The α-tocopherol loading reached 76.14% under the conditions of 35℃,18MPa and reaction time of 1h.

关 键 词：超临界二氧化碳注入法 Α-生育酚 介孔二氧化硅 

分 类 号：TS201.1[轻工技术与工程—食品科学]