蒸汽爆破预处理提高竹屑糖化效果的研究  

Study on improving the saccharification effect of bamboo sawdust by steam explosion pretreatment

作　　者：杨春柳 管秀琼 刘春 刘林培 YANG Chun-liu;GUAN Xiu-qiong;LIU Chun;LIU Lin-pei(School of Biological Engineering,Sichuan University of Science&Engineering,Zigong 643000,Sichuan,China;Biomass Energy Technology Research Center,Key Laboratory of Development and Application of Rural Renewable Energy Ministry of Agriculture and Rural Affairs,Biogas Institute of Ministry of Agriculture and Rural Affairs,Chengdu 610041,Sichuan,China)

机构地区：[1]四川轻化工大学生物工程学院,四川自贡643000 [2]农业农村部沼气科学研究所,农业农村部可再生能源开发与利用重点实验室,生物质能技术研究中心,四川成都610041

出　　处：《粮食与油脂》2023年第3期104-108,113,共6页Cereals & Oils

基　　金：四川省科技厅项目(2021ZHZY0015)。

摘　　要：采用蒸汽爆破法对制浆备料工段的竹屑进行预处理,探究其对竹屑水解糖化的影响,并对蒸汽爆破前后竹屑的色度、结构及组分进行对比分析。结果表明:最佳工艺条件为竹屑原料含水率55%、爆破压力2.5 MPa、维压时间180 s,在该条件下还原糖含量为12.50%,较未预处理竹屑提高了61.08%;纤维素含量提高了13.98%,且60.63%的半纤维素被保留下来;蒸汽爆破使得竹屑变得蓬松且颜色由黄棕色转为黄褐色,纤维表面出现撕裂现象;纤维主体结构没有改变,纤维素、半纤维素及酸不溶木素的部分结构被破坏,竹屑物料相对结晶度由49.46%增加到55.93%。The bamboo sawdust in the pulping and preparation section were pretreated by steam explosion method to explore its effect on the hydrolysis and saccharification of bamboo sawdust, and the chromaticity, structure and composition of bamboo sawdust before and after steam explosion were compared and analyzed. The results showed that the optimum technological conditions were as follows: the moisture content of bamboo sawdust 55 %, the bursting pressure 2.5 MPa, and the pressure maintaining time 180 s. Under this condition, the content of reducing sugar was 12.50 %, which was 61.08 % higher than that of untreated bamboo sawdust. The content of cellulose increased by 13.98 %, and 60.63 % of hemicellulose was retained. Steam explosion made the bamboo sawdust become fluffy and the color changed from yellow-brown to yellow-brown, and the fiber surface was torn. The main structure of the fiber remained unchanged, and the partial structures of cellulose, hemicellulose and acid-insoluble lignin were destroyed. The relative crystallinity of bamboo sawdust increased from 49.46 % to 55.93 %.

关 键 词：竹屑 蒸汽爆破法 还原糖含量 纤维结构 

分 类 号：TS201.1[轻工技术与工程—食品科学]